RockySea Petro Precision Rolling PipeRockySea Petro Petro manufactures Precision rolling pipe in China. We have our own factory of Precision rolling pipe. RockySea Petro Petro provide the high quality and competitive price on Precision rolling pipe for you. Contact us now for Precision rolling pipe quotation.It has various types of cold rolling mill such as LG30, LG60, LG80 , LG220 and establishes a complete quality Control system.RockySea Petro’s precision rolling pipe has extremely high precision and straightness ca
VIEW DETAILSRockySea Petro Coated Sucker RodWith the increase of working time, conventional sucker rods are prone to corrosion and eccentric wear during operation, and are not suitable for harsh working conditions. In 2012, RockySea Petro developed a fully coated sucker rod. By using HDPE resin to fully coat the sucker rod body, the anti-corrosion and anti-abrasion of the sucker rod is realized. And this tech of RockySea Petro has gained patent in China, Canada and the United States.Description It is the ideal matching
VIEW DETAILSRockySea Petro Onshore Thermal Recovery WellheadRockySea Petro has more than 40 years of experience in oil and gas wellhead & x-mas tree and valve production, with advanced manufacturing and testing equipment, can produce a variety of pressure levels, material levels, specification levels of well control equipment. After more than 20 years of development, Various types of thermal recovery wellhead & x-mas tree equipment have been formed, used in many oilfields in the world. RockySea Petro’s thermal recovery wel
VIEW DETAILSRockySea Petro Self-Propelled Carrier and TralierFeaturesRockySea Petro has developed a special workover rig chassis range from 6X6 to 14X14, which is compatible with the entire series of XJ250 to XJ850 workover machines. It can operate in various terrains such as roads, deserts, mountains, and swamps, with strong driving power, good off-road performance, and can work in the range of ambient temperature -45 ℃ to 50 ℃.Besides,the company also developed a desert off-road carrier. The driving type is
VIEW DETAILSRockySea Petro Casing Stop RingDatasheetUseWhen using the top thread stop ring, the following steps should be followed.1. When using the fixed screw type, first insert the sleeve, then insert the screw and use a hammer to strike.2. The conventional stop ring should be inserted into the sleeve first, and then the screw should be tightened with a wrench.3. Snap on the locking ring, directly attach the locking ring to the sleeve, lock it with a pin, and then tap in the screw.TypeThe stop rings of
VIEW DETAILS
Manufacturer of Tungsten Alloy Casing
Tungsten Alloy Casing | |||||
Type | Size(O.D. ) | Plating Parameters | |||
in | Mm | Layer thickness | Hardness | CASS | |
H40 J55 K55 L80 N80 C90 T95 P110 | 4 1/2 | 114.3 | ≥38um | 500-550HV(After heat treat:900-1000HV ) | No discoloration,pitting,cracks in 96 hours. |
5 | 127 | ||||
5 1/2 | 139.7 | ||||
6 5/8 | 168.28 | ||||
7 | 177.8 | ||||
7 5/8 | 193.68 | ||||
8 5/8 | 219.08 | ||||
9 5/8 | 244.48 | ||||
13 3/8 | 339.72 | ||||
Performance Parameters | |||||
Item | Parameter | ||||
Plating composition | Ni, P, W, Carbide (mass fraction) | ||||
Plating hardness | 50-550HV (plated state), 940-1100HV (heat treatment) | ||||
Wear resistance | 2-3 times better than chromium plating | ||||
Corrosion resistance | resistance to aggressive service like H2S, CO2, NaCI, HCI, etc. | ||||
Current efficiency | 80% -85% | ||||
Deposition rate | 35um-45um/h | ||||
Adhesion | 8Kg/mm2, plating no falling under high temperature and pressure. |
Tungsten Alloy Tubing | |||||
Type | Size(O.D. ) | Plating Parameters | |||
in | mm | Layer thickness | Hardness | CASS | |
NUE J55 L80 N80 P110 | 1.9 | 48.26 | ≥38um | 500-550HV (After heat treat:900-1000HV ) | No discoloration,pitting,cracks in 96 hours, |
2 3/8 | 60.32 | ||||
2 7/8 | 73.02 | ||||
3 ½ | 88.9 | ||||
4 1/2 | 114.3 | ||||
EUE J55 L80 N80 P110 | 1.9 | 48.26 | |||
2 3/8 | 60.32 | ||||
2 7/8 | 73.02 | ||||
3 ½ | 88.9 | ||||
4 1/2 | 114.3 | ||||
Performance Parameters | |||||
Item | Parameter | ||||
Plating composition | Ni, P, W, Carbide (mass fraction) | ||||
Plating hardness | 50-550HV (plated state), 940-1100HV (heat treatment) | ||||
Wear resistance | 2-3 times better than chromium plating | ||||
Corrosion resistance | resistance to aggressive service like H2S, CO2, NaCI, HCI, etc. | ||||
Current efficiency | 80% -85% | ||||
Deposition rate | 35um-45um / h | ||||
Adhesion | 8Kg/mm2, plating no falling under high temperature and pressure. |